single_project

AUSTIN PLATINUM PLUS

THE MOST DURABLE MARINE PLYWOOD

BS 1088 is the British Standard specification for marine plywood that applies to plywood produced with untreated tropical hardwood veneers that have a set level of resistance to fungal attack. These are the best in class durable plywood's available in the range.
Austin Platinum Plus plywood's are used in areas like traditional boat building to projects that require durable and high face grade panels.

  • Borrer Proof

  • Fire Retradant

  • Termite Proof

  • Years Warrenty

Specifications

#
Test
Requirments as per IS 710 : 2010
Test Results
01
Dimensional Tolerance
For3≤t≤12 mm thickness, tolerance in one panel : 0.6 mm
Tolerance in nominal thickness:
+(0.2+0.03t)
-(0.4+0.03t
For t>12 mm thickness, tolerance in one panel : 0.6 mm
Tolerance in nominal thickness:
+(0.2+0.03t)
-(0.4+0.03t)
With in limit
02
Tolerance in nominal length and width
±3.5 mm
1.0 mm
03
Tolerance on squareness and edge straightness
1 mm/m
0.5
04
Moisture Content
1 mm/m
0.5
04
Tolerance on squareness and edge straightness
Shall be between 6% to 14%
8 to 10 %
05
Quality of surface appearance
Shall not exceed the requirements of veneer for outer plies ( Face veneer)
With in limit
06
Manufacturing defects
Shall not contain following defects : Open joints ( e.g. core gaps , overlaps and pleats, blisters, hollows, bumps and imprints) , roughness ( other than due to the irregular structure of the wood) , sanding through , foreign particles , defects in the edge of the panels ( e.g. due to sanding , sawing , missing wood ).
Free from any kinds of defects
07
Bonding Quality
Mean shear Mean
Strength appearance
Wood failure
0.2 ≤ fv < 0.4 ≥ 80
0.4 ≤ fv < 0.6 ≥ 60

0.6 ≤ fv < 0.1.0 ≥ 40

1.0 ≤ fv no requirement
2.03
08
Density
Density of marine plywood at 12% moisture content shall be >500 Kg/m³
815 Kg/m³
09
Knife Test
Pass Standard
Excellent
10
Glue shear strength in Dry State, N
1350
1680
11
Water Resistance Test, N
1000
1320
12
Mycologocal Teat, N
1000
1280
13
Tensile Strength, Kgf/cm²
845
1103
14
Modulus of Elasticity along grain, N/mm²
7500
10150
15
Modulus of Elasticity across the grain,N/mm²
4000
6975
16
Modulus of rupture along , N/mm²
50
73.5
17
Modulus rupture across grain, N/mm²
30
58.35