Most Durable Marine Plywood

AUSTIN PLATINUM PLUS

THE MOST DURABLE MARINE PLYWOOD

Most Durable Marine Plywood. Designed by: Buyersinn.com

BS 1088 is the British Standard specification for marine plywood that applies to plywood produced with untreated tropical hardwood veneers that have a set level of resistance to fungal attack. These are the best in class durable plywood's available in the range.

Austin Platinum Plus plywood's are used in areas like traditional boat building to projects that require durable and high face grade panels.

SPECIFICATION

# TEST SPECIFIED IN BS 1088 TEST RESULT
1 Dimensional Tolerance For3≤t≤12 mm thickness, tolerance in one panel : 0.6 mm
Tolerance in nominal
thickness:
+(0.2+0.03t)
-(0.4+0.03t
For t>12 mm thickness, tolerance in one panel : 0.6 mm
Tolerance in nominal
thickness:
+(0.2+0.03t)
-(0.4+0.03t)
With in limit
2 Tolerance in nominal length and width ±3.5 mm 1.0 mm
3 Tolerance on squareness and edge straightness 1 mm/m 0.5
4 Moisture Content Shall be between 6% to 14% 8 to 10 %
5 Quality of surface appearance Shall not exceed the requirements of veneer for outer plies ( Face veneer) With in limit
6 Manufacturing defects Shall not contain following defects : Open joints ( e.g. core gaps , overlaps and pleats, blisters, hollows, bumps and imprints) , roughness ( other than due to the irregular structure of the wood) , sanding through , foreign particles , defects in the edge of the panels ( e.g. due to sanding , sawing , missing wood ). Free from any kinds of defects
7 Bonding Quality Mean shear Mean
Strength appearance
Wood failure
0.2≤fv<0.4 ≥80

0.4≤fv<0.6 ≥60

0.6≤fv<0.1.0 ≥40

1.0≤fv no requirement

2.03
8 Density Density of marine plywood at 12% moisture content shall be >500 Kg/m³ 815 Kg/m³
9 Knife Test Pass Standard Excellent
Additional Tests on BS 1088 Marine Plywood as per IS 710
10 Glue shear strength in Dry State, N 1350 1680
11 Water Resistance Test, N 1000 1320
12 Mycologocal Teat, N 1000 1280
13 Tensile Strength, Kgf/cm² 845 1103
14 Modulus of Elasticity along grain, N/mm² 7500 10150
15 Modulus of Elasticity across the grain,N/mm² 4000 6975
16 Modulus of rupture along , N/mm² 50 73.5
17 Modulus rupture across grain, N/mm² 30 58.35